| Catalysis of nanocomposite CuO·Cr2O3 on thermal decomposition of RDX |
|
HONG Wei liang,LIU Jian hong,TIAN De yu,GUI Yang,REN Xiang zhong,ZHAO Feng qi
|
|
1.Dept. of Chemistry and Biology, Normal Coll., Shenzhen Univ., Shenzhen 518060, China;2.Inst. of Aerospace and Material Engineering, National Univ. of Defence Technology, Changsha 410073, China;3.Xi’an Modern Chemistry Research Inst., Xi’an710065, China
|
| Abstract: |
| Nanocomposite oxide CuO·Cr 2O 3 with different mass ratio of Cu and Cr was synthesized by solid state reaction method at room temperature, and dispersing agent was added to disperse nanometer particle. The particle size, crystal form, and phase were examined with XRD and TEM. Average particle size were about 15 nm. The catalytic performance of nanocomposite oxide CuO·Cr 2O 3 was determined by DSC. The results show that the peak temperature of thermal decomposition of RDX decrease 11 1℃, under the effect of nanocomposite oxide CuO·Cr 2O 3, and the apparent activation energy of the thermal decomposition of RDX decrease 17kJ/mol. The catalytic action of nanocomposite oxide CuO·Cr 2O 3 is better than that of nanometer Cr 2O 3 and its mixture. |
| Key words: Nitramine propellant Nanocomposite oxide Thermal decomposition Combustion catalyst |